Place of Origin: | P.R. China |
---|---|
Brand Name: | FOTMA |
Certification: | ISO9001:2008 |
Model Number: | WNiFe, WNiCu |
Minimum Order Quantity: | 1 pcs |
Price: | Negotiable |
Packaging Details: | Paper cartons or plywood boxes |
Delivery Time: | 20-25 days after deposit |
Payment Terms: | T/T, L/C, Western Union, PayPal |
Supply Ability: | 10000pcs/month |
Tungsten Purity: | 90% To 98% | Others: | Ni Fe Or Ni Cu |
---|---|---|---|
Thickness: | 0.06 - 100mm | Surface: | Machined |
Density: | 17.1 - 18.5 G/cc | Tolerance: | +/-0.05 - 0.1mm |
High Light: | 17.7g/cm3 Tungsten Heavy Alloy Tablet,WNiFe WNiCu Tungsten Alloy Tablet,0.06mm Tungsten Heavy Alloy Tablet |
Tablets Tungsten Heavy Alloy WNiFe WNiCu Density 17 - 18.5g / cm3 Machined
Tungsten heavy alloy is a suitable raw material for radiation protection, as its combination of radiographic density (more than 60% denser than lead), machinability, good corrosion resistance, high radiation absorption (superior to lead), simplified life cycle and high strength. WHA typically consists of 90 to 98 wt% W in combination with some mix of nickel, iron, copper, and/or cobalt. The bulk of alloy production falls into the 90 to 95% W range. Density of WHAs varies from 17.7g/cm3 to 18.5g/cm3.
The majority of current uses for WHAs are best satisfied with the W-Ni-Fe system. such as 93W-4.9Ni-2.lFe and 95W-4Ni-lFe represent common compositions. The addition of cobalt to a W-Ni-Fe is a common approach for slight enhancement of both strength and ductility.
The presence of cobalt provides solid-solution strengthening of the binder and slightly enhanced tungsten-matrix interfacial strength. Cobalt additions of 5 to 15% of the nominal binder weight fraction arc most common.
Introduction of Tungsten Heavy Alloy Tablets:
Standard: AMS-T-21014
Density: (17.7 - 18.5) g/cm3
Main Component: W (90 - 97)% with Ni & Fe or Ni & Cu
Thickness: 0.06mm to 100mm
Width x Length: Max 300 x 600mm
Surface Condition: Machined, Ground
Mechanical Properties of Tungsten Heavy Alloys:
AMST 21014 class 1
90%WNiFe, 90%WNiCu
Density : 17.0
Hardness: 32HRC max
Elongation: 5 - 20%
AMST 21014 class 2
92.5%WNiFe, 92.5%WNiCu
Density : 17.5
Hardness: 33HRC max
Elongation: 5 - 15%
AMST 21014 class 3
95%WNiFe, 95%WNiCu
Density : 18.0
Hardness: 34HRC max
Elongation: 3 - 10%
AMST 21014 class 4
97.5%WNiFe, 97.5%WNiCu
Density : 18.5
Hardness: 35HRC max
Elongation: 1 - 8%
Tungsten Alloy Tablets Applications:
Protection shields for nuclear radiation.
The war industry with the ball core,the ball link.the shrapnel,the armor-piercing shell uses the ball
Balancing weights
Electrodes for Resistance Weldingt tungsten alloy
High voltage electrical contact
Specifications of Tungsten Heavy Alloys:
Table 1. Properties of tungsten alloy ( AMS-T-21014 )
Class | Nominal tungsten (weight percent) | Density (g/cc) | Hardness ( HRC )(maximum) |
1 | 90 | 16.85 - 17.25 | 32 |
2 | 92.5 | 17.15– 17.85 | 33 |
3 | 95 | 17.75– 18.35 | 34 |
4 | 97 | 18.25– 18.85 | 35 |
Table 2. Mechanical Properties – Minimum Value ( AMS-T-21014 )
Class | Ultimate tensile strength ( ksi) | Yield strength at 0.2percent offset (ksi) | Elongation( percent ) |
1 | 110 | 75 | 5 |
2 | 110 | 75 | 5 |
3 | 105 | 75 | 3 |
4 | 100 | 75 | 2 |
Picture show: