Place of Origin: | P.R.China |
---|---|
Brand Name: | FOTMA |
Certification: | ISO 9001: 2008 |
Model Number: | High Pressure Pump Components |
Minimum Order Quantity: | 1 pc |
Price: | Negotiable |
Packaging Details: | In plywood boxes |
Delivery Time: | 20-25 days after deposit |
Payment Terms: | T/T |
Supply Ability: | 1MT/month |
Grades: | YG6, YG8 Etc. | OEM: | Available |
---|---|---|---|
Sizes: | Customized | Condition: | Machined, Ground |
Grain Size: | Average | Application:: | High Pressure Pump Components |
Highlight: | YG8 Tungsten Carbide Seal Rings,10mm Tungsten Carbide Seal Rings,FOTMA 10mm tungsten carbide seal |
Tungsten Carbide Wear Parts Carbide High Pressure Pump Seals Components Dia. 10mm
Tungsten Carbide Seals are used as Mechanical Seal faces in high pressure pumps, Compressors and Agitators. These are used in Oil Refineries, Petrochemical plants, Fertilizer Plants, and Drugs/Pharmaceutical Industries.
Features of Carbide Seals Components:
Mechanical seal components are developed to withstand high temperature, high pressure & highly corrosive chemical attack. We manufacture Rings in various shapes like Plain Ring, DA type, T-shape, L-shape and in shapes as per customers requirement.
Tungsten Carbide Seal Rings are generally made with Cobalt as binder material. Nickel bonded Rings also can be supplied.
Advantages of Carbide Seal Rings:
1. Professional producer and OEM service
2. Sealing effects
3. Easy replacement
4. Customized mold
5. Quality management system
6. Exquisite packaging
7. Wide application
8. Drawing will be provided for free with mass production products
Recommended Material Grade for High Pressure Pump Compnents:
Density (g/cm3) |
14˜15 |
Hardness (HRA) |
87-91 |
Elastic Modulus (MPa) |
608100 |
Bend Strength (MPa) |
1420-2058 |
Coefficient of heat Expansion |
4.5-6.3 |
Thermal Condutivity (cal/cm.s. °c) |
0.17 |
Type |
YG6 |
YG8 |
WC-10% (Ni-Cr) |
90%Acetic-Acid+1%Cobalt Acetate 120°c,193Hours |
- |
67.2 |
28.8 |
15%Acetic-Acid 40°c, 144Hours |
45.48 |
113.42 |
9.16 |
98%Acetic-Acid 40°c, 100Hours |
22.75 |
31.68 |
1.74 |
37%Hydrochiloric ACID, 40°c, 144Hours |
191 |
264 |
42.2 |
Grade |
ISO |
Density |
HRA |
Bending Strength |
YG3X |
K01 |
15.1-15.3 |
93.6 |
1450 |
YG3 |
K01 |
15.1-15.3 |
92.4 |
1700 |
YG6X |
K10 |
14.8-15.0 |
92.5 |
2100 |
YG6A |
K10 |
14.8-15.0 |
93.0 |
1850 |
YG6 |
K20 |
14.9-15.1 |
91.1 |
2500 |
YG8 |
K20-30 |
14.6-14.9 |
90.3 |
2800 |
YG15 |
K40 |
14.0-14.2 |
88.0 |
2300 |